High Atmosphere Temperature Hn Apm Resistance Wire used for Furnace Elements

Basic Info.

Model NO.	APM
Flat Stirp T	0.5-2.5mm
Flat Wire W	0.5-4.5mm
Elongation	15%-25%
Max Continuous Service Temperatu	1425c
Resisivity	1.45
Surface	Bright
Melting Point	1500 C
Density(G/Cm 3 )	7.1
Hardness	220-260 Hv
Transport Package	Wooden Case, Wooden Pallet
Specification	0.5 ~ 10 mm, ISO9001, ISO14001
Trademark	Huona
Origin	China
HS Code	85169090
Production Capacity	2000ton/Year

Product Description

High atmosphere temperature APM Resistance Wire used for Furnace elementsThis product takes refined master alloy as raw material, uses powder metallurgy technology to manufacture alloy ingots, and is manufactured by special cold and hot processing and heat treatment process. The product has the advantages of strong oxidation resistance, good corrosion resistance at high temperature, small creep of electrothermal components, long service life at high temperature and small change of resistance. It is suitable for high temperature 1420 C, high power density, corrosive atmosphere, carbon atmosphere and other working environments. It can be used in ceramic kilns, high temperature heat treatment furnaces, laboratory furnaces, electronic industrial furnaces and diffusion furnaces.
AdvantagesHigh atmosphere temperature Long lifeHigh surface load Good oxidation resistanceSmall proportion High resistivityGood sulfur resistance
Specifications
Wire diameter range : φ0.1-8.5 mm
Flat Wire Thickness : 0.1-0.4 mm Width:0.5-4.5 mm
Flat Strip Thickness : 0.5-2.5 mm Width:5.0-48 mm
Main composition(Wt%)

	C	Si	Mn	Cr	Al	Fe
Min	-	-	-	20	5.5	Bal.
Max	0.04	0.5	0.4	22	6.0	Bal.

Main mechanical properties

Tensile Strength at Room Tmperature	Elongation	Hardness	Tensile Strength at 1000ºC	High Temperature Durability At 1000ºC and 6 Mpa
650-750 Mpa	15-25%	HV220-260	22-27Mpa	≥100h

Main physical properties

Density	Resistivity	Melting Point	Maximum Continuous Working Temperature
7.1g/cm³	1.45x10^-6Ω.m	1500ºC	1400ºC

Resistance Temperature Coefficient(Ct)

800ºC	1000ºC	1400ºC
1.03	1.04	1.05

Average Linear Expansion Coefficient

20-800ºC	20-1000ºC	20-1400ºC
14	15	16

Fast Life

	1300ºC	1350ºC
Average Fast Life (Hours)	110	90
Sagging rate after rupture	8	11

Testing according to GB/T13300-91 Standard Method